LCP 日本新石油化学 HM-402 BH-物性参数
性能项目 | 测试条件 | 测试方法 | 数值/描述 | 单位 | |
机械性能 | 拉伸强度(引张强度) | ASTM D638/ISO 527 | 143 | kg/cm²(MPa)[Lb/in2] | |
拉伸模量 | ASTM D638/ISO 527 | 1.3 | kg/cm²(MPa)[Lb/in2] | ||
拉伸屈服伸长率(延伸率) | ASTM D638/ISO 527 | 18.4 | % | ||
拉伸断裂伸长率(延伸率) | ASTM D638/ISO 527 | 15.3 | % | ||
弯曲模量(弯曲弹性率) | ASTM D790/ISO 178 | 0.46 | kg/cm²(MPa)[Lb/in2] | ||
弯曲强度 | ASTM D790/ISO 178 | 196 | kg/cm²(MPa)[Lb/in2] | ||
IZOD 缺口冲击强度 | 1/4" 23℃ | ASTM D256/ISO 179 | 38 | kg・cm/cm(J/M)ft・lb/in | |
1/4" -30℃ | ASTM D256/ISO 179 | kg・cm/cm(J/M)ft・lb/in | |||
1/8" 23℃ | ASTM D256/ISO 179 | kg・cm/cm(J/M)ft・lb/in | |||
1/8" -30℃ | ASTM D256/ISO 179 | kg・cm/cm(J/M)ft・lb/in | |||
Charpy冲击强度 | 23℃ (缺口) | ASTM D256/ISO 179 | 105 | kg・cm/cm(J/M)ft・lb/in | |
-30℃(缺口) | ASTM D256/ISO 179 | kg・cm/cm(J/M)ft・lb/in | |||
23℃(无缺口) | ASTM D256/ISO 179 | kg・cm/cm(J/M)ft・lb/in | |||
-30℃(无缺口) | ASTM D256/ISO 179 | kg・cm/cm(J/M)ft・lb/in | |||
物性性能 | 比重(密度) | ASTM D792/ISO 1183 | 1.70 | ||
吸水率 23℃/24H | ASTM D570/ISO 62 | 0.02 | % | ||
热性能 | 热变形温度 | 退火 | ASTM D648/ISO 75 | 310 | ℃(�) |
未退火 | ASTM D648/ISO 75 | ℃(�) | |||
熔点 | - | ℃(�) | |||
燃烧性(率) | UL94 | 25 | |||
线性膨胀系数 | ASTM D696/ISO 11359 | 18.1 | mm/mm.℃ | ||
电气性能 | 介电常数 | 100HZ | ASTM D150/IEC 60250 | ||
1MHZ | ASTM D150/IEC 60250 | ||||
介电损耗 | 100HZ | ASTM D150/IEC 60250 | |||
1MHZ | ASTM D150/IEC 60250 | ||||
体积电阻率 | ASTM D257/IEC 60093 | Ω.cm | |||
表面电阻率 | ASTM D257/IEC 60093 | Ω | |||
耐电弧性 | ASTM D495/IEC 60112 | ||||
加工条件 | 干燥条件 | ||||
加工温度 | 射嘴 | ℃ | |||
料筒前段 | ℃ | ||||
料筒中段 | ℃ | ||||
料筒后段 | ℃ | ||||
熔体温度 | ℃ | ||||
模具温度 | ℃ | ||||
压力 | 注塑压力 | Mpa | |||
保压压力 | Mpa | ||||
背压 | Mpa | ||||
螺杆转速 | rpm | ||||
其他 | 备注 | 高耐热310度 高刚性 | |||
颜色 | 黑色 | ||||
特性 | 高耐热310度 高刚性 | ||||
用途 | 连接器 |